| Properties |
Method |
Unit |
|
| Specific gravitiy |
ISO 1183 |
g/cm3 |
1,13 |
| Water Absorption |
DIN 53495 |
% |
3 |
| Chemical Resistance |
X |
X |
X |
| Max. permissible service temperature |
- |
°C |
plus 70 |
| Min. permissible service temperature |
- |
°C |
-40 |
| Tensile strength at yeild |
ISO 527 |
MPa |
90/45 |
| Elongation at yeild |
ISO 527 |
% |
4,5/20 |
| Tensile strength at break |
ISO 527 |
MPa |
X |
| Elongation at break |
ISO 527 |
% |
<50 |
| Impact Strength |
ISO 179 |
kJ/m2 |
o.B. |
| Notch Impact Strength |
ISO 179 |
kJ/m2 |
9/o.B. |
| Ball indication hardn. (Hk)/Rockwell |
ISO 1239-1 |
MPa |
160/70 |
| Shore-D |
DIN 53505 |
|
77 |
| Flexural strength |
ISO 178 |
MPa |
X |
| Modulus of elasticity |
ISO 527 |
MPa |
3000/1000 |
| Vicat softening temp. VST/B/50 VST/A/50 |
ISO 306 |
°C |
X |
| Heat deflection temperature HDT/B HDT/A |
ISO 75 |
°C |
plus 160 |
| Coef. of linear therm. expansion |
DIN 53752 |
K-1x 10-4 |
0,85 |
| Thermal conductivity at plus 20°C |
DIN 52612 |
W/(m x K) |
0,28 |
| Volume resistivity |
VDE 0303 |
x cm |
1013 / 1010 |
| Surface resistivity |
VDE 0303 |
|
- / 1010 |
| Dielectric constant at 1 MHz |
DIN 53483 |
|
3,5/7 |
| Diel. loss factor at 1 MHz |
DIN 53483 |
|
0,031/0,3 |
| Dielectric strength |
VDE 0303 |
KV/mm |
20-50 |
| Tracking resistance |
DIN 53480 |
|
CTI600 |
| Bondability |
|
|
YES |
| Physiological indifference according |
EEC 90/128 FDA |
|
YES |
| Friction coefficient |
DIN 53375 |
|
0,38-0,45 |
| Flammability |
UL 94 |
|
HB |
| UV stabilisation |
|
|
X |
| Acid resistance |
|
|
X |
| Hydroxid resistance(delute) |
|
|
YES |
| Hydrocarbonat resistance |
|
|
+/0 |
| CKW resistance |
|
|
X |
| Aromatic resistance |
|
|
+/0 |
| Ketone resistance |
|
|
YES |
| Resistance against hot water |
|
|
+/0 |